The Influence of Excitation Method on the Strength of Glass Powder High-Strength Cementitious Materials

Recycling economy and the re-utilization of solid waste have become important parts of sustainable development strategy. To improve the utilization rate of waste glass, glass powder high-strength cementitious material (GHSC) was prepared by replacing part of the cement in the cementitious material with ground waste glass powder. Firstly, the effect of glass powder particle size on the flexural and compressive strength of GHSC was investigated by the gray correlation method, and the optimal grinding time was obtained. Additionally, the effect of the magnitude of steam curing temperature and the length of steam curing time on the compressive strength and flexural strength of GHSC was investigated, and the mechanism of the effect of the curing regime on the strength was explored by examination of the microstructure. Finally, to simplify the curing process of GHSC, the effects of Ca(OH)2 and Na2SO4 as excitation agents on the compressive strength and flexural strength of GHSC at different dosing levels were compared. The results showed that glass powder with a particle size of less than 20 μm would improve the compressive strength and flexural strength of the specimen. Steam curing can significantly improve the flexural strength and compressive strength of GHSC specimens. At a steam curing temperature of 90 °C for a duration of three days, the compressive strength and flexural strength of GHSC increased by 76.7% and 98.2%, respectively, compared with the standard curing specimens. Ca(OH)2 and Na2SO4 as excitation agents significantly enhanced the compressive and flexural strengths of GHSC under standard curing conditions.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.